Heat Control Filters
主な用途（共通）
- コピー機
- 外科・歯科照明
- 科学機器［計器］
Ultraviolet Cold Mirrors
| Thickness | 3.0 mm ±0.5 mm |
|---|---|
| Size Tolerance | +0.0 mm/-0.5 mm |
| Min. Clear Aperture | 95% of outside dimension |
| Substrate Material | Borosilicate glass |
| Flatness | 5–10 waves per 25 mm |
| Parallelism | 3 arc minutes or better |
| Surface Quality | 80/50 per MIL-O-13830 |
| Humidity and Abrasion | Per MIL-C-675A |
| Max. Operating Temperature | +200℃ |
| Mechanical | Unmounted |
Cold Mirrors
| Thickness | 3.0 mm ±0.5 mm |
|---|---|
| Size Tolerance | +0.0 mm/-0.5 mm |
| Min. Clear Aperture | 95% of outside dimension |
| Substrate Material | Borosilicate glass |
| Flatness | 5–10 waves per 25 mm |
| Parallelism | 3 arc minutes or better |
| Surface Quality | 80/50 per MIL-O-13830 |
| Humidity and Abrasion | Per MIL-C-675A |
| Max. Operating Temperature | +200℃ |
| Mechanical: Unmounted | – |
Hot Mirrors
| Thickness | 3.0 mm ±0.5 mm |
|---|---|
| Size Tolerance | +0.0 mm/-0.5 mm |
| Min. Clear Aperture | 95% of outside dimension |
| Substrate Material | Borosilicate glass |
| Flatness | 5–10 waves per 25mm |
| Parallelism | 3 arc minutes or better |
| Surface Quality | 80/50 per MIL-O-13830 |
| Humidity and Abrasion | Per MIL-C-675A |
| Max. Operating Temperature | +200℃ |
| Mechanical: Unmounted | – |
Infrared Suppressing Filters
| Thickness | 6.0 mm ±0.5 mm |
|---|---|
| Size Tolerance | +0.0 mm/-0.5 mm |
| Min. Clear Aperture | 95% of outside dimension |
| Substrate Material | Borosilicate glass |
| Flatness | 5–10 waves per 25mm |
| Parallelism | 3 arc minutes or better |
| Surface Quality | 80/50 per MIL-O-13830 |
| Humidity and Abrasion | Per MIL-C-675A |
| Max. Operating Temperature | +100℃ |
| Mechanical: Unmounted | – |